Product Name

Unit

Test Method

Condition

B100

B100EX

B703

B706

B706C

B7010

B801

B9000EP

B9706EP

B9706PBK

Modified Categories

——

——

——

General PA6

Extrusion Grade PA6

Glass Fiber Reinforced PA6

 Toughened PA6

Flame Retardant PA6

1. Density

g/cm³

ISO 1183

Dry

1.13

1.1

1.23

1.36

1.26

1.55

1.03

1.23

1.52

1.40

2.  24H Water Absorb(23℃，50%Relative Humidity)

%

ISO 62

1.7-2.1

1.4-2.0

.9-2.3

1.0-1.4

1.0-1.4

0.8-1.2

0.5-0.9

1.0-1.4

0.7-1.1

0.7-1.1

3. Saturated Water Absorption（In water）

%

ISO 62

9-10

9-10

6-7

5-7

5-7

3-5

7-8

8-9

5-6

5-6

 Mechanical Properties

4. Tensile Stress

MPa

ISO 527

Dry/Wet

74/45

50/35

110/60

170/110

190

220/170

60/37

70/45

155/-

130/-

5. Elongation at Break

%

ISO 527

Dry/Wet

20/40

——

3/5

3/5

3/5

2.0/3.5

35/50

-

3/-

3/-

6. Flexural Stress

MPa

ISO 178

Dry/Wet

95/45

30/-

160-80

220/170

250/-

300/200

55/-

85/-

200/-

200/-

7. Flexural Modulus

MPa

ISO 178

Dry/Wet

2550/850

750/-

4000/2200

7500/5000

14000/-

13000/9000

1550/685

2700/-

8500/-

8000/-

8.  Notched Izod Impact Strength

KJ/m²

ISO 180

Dry/Wet

4.5/16

60/NB

10/16

13/20

13/20

16/25

80/NB

5/10

8.5/-

10/-

9. Hardness Rockwell

R

ISO 2039/2

Dry/Wet

118/97

100/-

120/114

120/114

120/114

120/115

100/-

120/105

120/-

120/-

Thermal Properties

10. Heat Deflection Temperature (0.45MPa)

℃

ISO 75

170

160

210

220

220

220

130

200

215

215

 Heat Deflection Temperature (1.80MPa)

℃

ISO 75

60

60

190

205

205

215

55

60

190

190

11.Linear Therma Expansion

10^-5/K

ASTM D696

Dry/Wet

2-3/6-7

12. Injection Molding Temperature

℃

250-270

230-250

260-290

260-290

260-290

270-290

270-290

225-250

245-270

245-270

13. Linear Molding Shrinkage (flow diretion)

%

ISO2577

Dry

1.0-1.4

0.9-1.3

0.2-0.6

0.2-0.5

0.2-0.5

0.1-0.3

0.6-1.0

1.0-1.3

0.1-0.3

0.1-0.4

14.   Melt Flow Rate

g/10min

ISO 1133

Dry

3-4

15. Mold Temperature

℃

40-60

——

80-90

80-90

80-90

80-90

40-60

40-60

80-90

80-90

16.  Melt Point

℃

DSC法

220

220

220

220

220

220

220

220

220

220

Electrical Properties

17. Surface Resistivity

Ω

ASTM D257

Dry/Wet

10¹³/10¹⁰

10¹³/10¹⁰

10¹³/10¹⁰

10¹²/10¹⁰

10⁴/-

10¹³/10¹⁰

10¹³/10¹⁰

10¹²/10¹⁰

10¹²/10¹⁰

10¹²/10¹⁰

18. Dielectric Strength

KV/mm

ASTM D149

Dry/Wet

20/-

20/-

17/-

17/-

-/-

17/-

20/-

17/-

17/-

17/-

19. Fire Retardant Rating(1/16 inch)

UL-94

V-2

HB

HB

HB

HB

HB

HB

v-0

V-0

v-0

20. Use

Bandage, Coil Frame

Nylon Core Material, Double-Walled Nylon Bellows

Mechanical Parts, Electric Tool Shell, Fishing Gear, Coil Skeleton, Auto Parts, Railway Components, Automotive Hood Cover, Automotive Intake Manifold, Internal and External Components of Large Aircraft Cabin

Electric Welding Mask，Automotive Shock Absorber Sleeve，Wheel Housing，socket connectors

Electronic Components, Electrical Terminals, Circuit Breakers, Circuit Switches